ASA LIGHT WEIGHT - 750g/spool
99.00 Lei
Selectează culoarea
Descriere
ASA Light-Weight Filament offers exceptional dimensional accuracy at 1.75mm±0.03mm, ensuring smooth 3D printing with minimal jams. Its 750g spool provides ample material for projects, while the lightweight nature reduces printer load, enhancing efficiency. ASA's inherent weather resistance and durability make this filament ideal for both indoor and outdoor 3D prints, boosting versatility.
Livrare gratuită la comenzi peste 250 Lei
Politică de returnare 30 de zile
Procesare comenzi securizată
Descriere detaliată
Light Weight ASA
The Eryone ASA lightweight filament is a high-performance 3D printing material that
combines high toughness, impact resistance, and ultra-lightweight, low-density characteristics, making it particularly suitable for applications such as aircraft models and outdoor models that demand high strength and low weight. Its excellent water resistance and UV protection ensure long-term stability in outdoor environments, avoiding the common issues of brittleness and degradation seen in PLA materials. The printed surface features a fine matte finish with minimal stringing and easy post-processing. With a heat deflection temperature of approximately 80°C, it maintains structural stability at higher temperatures, making it an ideal choice that surpasses PLA lightweight materials.
Part I:Suggests Printing Parameters
| Parameter | Set up |
| Nozzle temperature | 200-280 ℃ |
| Bed temperature | 80-100℃ |
| Bed materia | glass, PEI, spring steel plate |
| Bottom printing temperature | 220-280 ℃ |
| Sealed printing | Supports open printing; better results with enclosure. |
| Printing speed | 30-100mm/s |
| Drying conditions | 80-90℃, 10h |
Part II: Physical Properties of Materials
| Property | Testing Method | Unit | Typical Value |
| Density(g/cm³ at 21.5 ° C） | ASTM D792 (ISO 1183, GB/T 1033) | g/cm³ | 0.99 |
| Vicat Softening Temperature(° C) | ASTM D1525 (ISO 306 GB/T 1633) | ℃ | 75 |
| Heat distortion temperature(° C) | ASTM D648 1.8MPa 0.45MPa | ℃ | 72 |
| Glass transition temperature (° C) | DSC, 10 ° C/min | ℃ | 64 |
| Melt Index(g/10 min) | 220 ° C, 10kg 240 ° C, 2.16 kg | g/10min | 36 |
Part III: Mechanical Properties of Printed Samples
| Property | Test conditions | Test standards | unit | Typical Value |
| Tensile strength X-Y | 50mm/min | GB/T 1040.4 | MPa | 16.1 |
| Elastic modulus X-Y | 50mm/min | GB/T 1040.1-2006 | MPa | 972.4 |
| Elongation at break X-Y | 50mm/min | GB/T 1040.4 | MPa | 8.1 |
| Tensile strength X-Z | 50mm/min | GB/T 1843 | MPa | 8.3 |
| Elastic modulus X-Z | 50mm/min | GB/T 1040.1-2006 | MPa | 758.3 |
| Elongation at break X-Z | 50mm/min | GB/T 1040.4 | % | 7.5 |
| Bending strength | 2mm/min | GB/T 9341 | MPa | 27.5 |
| Bending modulus | 2mm/min | GB/T 9341 | MPa | 1389.6 |
| Charpy Impact strenght | 2.75J | GB/T 1843 | kJ/m2 | 4.1 |
Note: All splines are printed under the following conditions: printing temperature=250 ° C, printing speed=80mm/s, base plate 60° C, filling=100%, nozzle diameter=0.4mm
High quality
Low density, light weight, strong adhesion, excellent matte surface and other characteristics, very suitable for other important fields such as model airplanes, ship models, to meet more printing scenarios.
Smooth Printing
Low shrinkage of printing molding, delicate surface, strong adhesion between layers, smooth printing, no warping edge cracking and other problems.
Special Technology
ERYONE Filament adopts a special modification method and adopts nano foaming technology, which greatly improves the foaming rate of PLA material without affecting the printing effect of PLA material, and the foaming rate can reach more than 200%.
Vacuum packing
Neat arrangement, high quality, vacuum packing, moisture-proof